ALCOPON-FILM

Joint venture «AND-POLIC» produces a multi-layer high-adhesive polymer film «ALCOPON - FILM» from 2010.

 

The multi-layer high-adhesive polymer film «ALCOPON - FILM» is produced by extrusion, followed by pneumatic dilation, is designed for bonding polyethylene bases with metal. The film is a three-layer polymer film, with the introduction of an adhesive base in one of the layers, which is a barrier, the other filter - dosing. In the production of films are used high quality raw materials of European manufacturers, as well as local production.

 

Scope: Production of Aluminum-plastic composite panels.

The products are identified by the national certification system for the Republic of Uzbekistan № UZ. SMT.01.178.1070781 and complies with the company standart Kst 64-19209760-001:2011. Product is made and supplied under ISO-9001:2008 Quality System.

The film is produced with a thickness of 0.03 mm to 0.06 mm and a width of up to 1520.0 mm.

Currently, films delivering to the ACP manufacturers in the Russian Federation and Iran. In addition, since 2010, the film uses for its own needs of the enterprise - in the production of Aluminum Composite Panels "ALCOPON".

 

CHARACTERISTICS AND PHYSICAL PROPERTIES OF MULTY-LAYER HIGH ADHESIVE POLYMER FILM «ALCOPON - FILM»

 

Item

ALCOPON – FILM

Thickness

0.03-0.06mm+0.005mm

Width

1250mm~1520mm+3mm

External diametr of roll

less than 280 mm

Length of film in 1 roll

less than 2500 m

Diametr of the spool

75 mm

Appearance

Connatural film

Package

Export packing according to the standart of enterprice KSt 64-19209760-001:2011

Tensile strength:

- in longitudinal direction

- in transverse direction

 

12,7 Mpa

13,7 Mpa

Elongation at break:

- in longitudinal direction

- in transverse direction

 

250 %

350 %

Melt flow rate

2,3 g/10 min(190ºC)

Density

0,92 g/cm3

Softening point

70ºC

Melting point

91ºC

Adhesion condition

120ºC ~ 150ºC (in rear side of aluminum coil)

Heating method

Hot metal roll pressing (lamination)

Stock time

12 months (keep dryness, aeration, waterproof)

Stock temperature

Room temperature